This NEW, globally available MOLYKOTE® AFC offers high-temperature welding prevention, excellent heat resistance, and good acid and coolant resistance.

High-temperature resistance and microsealing property; optimized for coil coating
Responding to market needs and trends toward reduced emissions

As emission standards become more stringent, manufacturers face tough lubrication challenges. MOLYKOTE®D-6900 Anti-Friction Coating provides excellent lubrication and high-temperature resistance, and it delivers a micro sealing property.

In addition,MOLYKOTE®D-6900 Coating can be coil-coated at a desired film thickness of 16-20 µm,allowing OEMs to produce metal gaskets, such as exhaust manifold gaskets (EMGs) that can help them achieve emission reduction targets and meet EURO 6 specifications.

Excellent heat resistance

Ball on plate test: Similar wear scar widths at 600°C and 700°C indicate resistance of MOLYKOTE® D-6900 AFC up to 700°C in the absence of oxygen

Meet emission specifications MOLYKOTE®D-6900 Anti-Friction Coating offers:
  • Micro Sealing property
  • High-temperature welding prevention
  • Excellent heat resistance
  • Good acid and coolant resistance

Globally available, MOLYKOTE®D-6900 Anti-Friction Coating – an NMP/NEP-free AFC – is optimized for coil coating. Exhaust manifold gaskets coated with MOLYKOTE®D-6900 Coating fulfill EURO 6 emission specifications, even at 600°C. Laboratory tests indicate full functionality up to 700°C, as shown in the table at right.

MOLYKOTE®D-6900 Coating prevents welding of metal/metal combinations at high temperatures and can be used in sliding contact of metal/metal combinations with slow to moderately fast movements and high loads.

Features
  • Excellent lubrication
  • Good acid resistance
  • Good solvent resistance
  • High load-carrying capacity
  • Excellent adhesion to metal
  • Low coefficient of friction
  • High resistance to motor oil and coolant
  • Excellent heat resistance
  • Suitable for coil coating
  • NEP/NMP-free
Composition
  • Solid lubricants
  • Organic binders
  • Organic solvents
Applications
  • Metal gaskets with high-temperature-resistance property(e.g.,exhaust manifold gaskets). Coating offers micro sealing property(fulfilling EURO 6 emission specifications up to 600°C)and prevents welding of metal/metal combinations at high temperatures. (NOTE: Temperatures above 600°C have not yet been tested.)
  • Sliding contact of metal/metal combinations with slow tomoderately fast movements and high loads.
How to use
Surface preparation

First,thoroughly clean and degrease the surface that will be coated with MOLYKOTE®D-6900 Anti-Friction Coating.Phosphating or sandblasting (100/180 grit–80/130 μm)increases the adhesion and service life.

How to apply

Stir MOLYKOTE®D-6900 Anti-Friction Coating thoroughly before applying by coil coating or screen printing. Recommended dry film thickness: 10to 20 µm (mean value).

Curing

Recommended curing conditions: 30 minutes at 200°C (392°F).However,curingtimedependssubstrate material, size, mass,coating thickness and type of curing system.

Dilution

Viscosity of MOLYKOTE®D-6900 Anti-Friction Coating can be decreased with MOLYKOTE® L-13 Thinner.

Coverage

1Kg of MOLYKOTE®D-6900 Anti-Friction Coating can cover up to 17m2.This calculation is based on a15 μm thick MOLYKOTE®D-6900 Anti-Friction Coating dry film and does not take into account the losses generated during the application process.